Product Data Sheet &
General Processing Conditions
RTP 300 FR A
Polycarbonate (PC)
Unreinforced
Flame Retardant
Non-PBBO/E
UL94 V-0
The RTP 300 FR A familiy of materials offer dimensional stability, rigidity, heat resistance, ignition resistance and excellent impact strength.
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS
PERMANENCE
English
SI Metric
ASTM
TEST
Specific Gravity
1.21
1.21
D 792
Melt Flow Rate
@ 300 °C, / 1.2 kg
10.00 - 12.00 g/10 min
10.00 - 12.00 g/10 min
D 1238
Molding Shrinkage
1/8 in (3.2 mm) section
0.0060 - 0.0090 in/in
0.60 - 0.90 %
D 955
Water Absorption, 24 hrs @ 23°C
0.150 %
0.150 %
D 570
MECHANICAL
Impact Strength, Izod
notched 1/8 in (3.2 mm) section
12.0 ft-lbs/in
641 J/m
D 256
unnotched 1/8 in (3.2 mm) section
No Break
No Break
D 4812
Tensile Strength
8400 psi
58 MPa
D 638
Tensile Elongation
> 10.0 %
> 10.0 %
D 638
Tensile Modulus
0.33 x 10^6 psi
2275 MPa
D 638
Flexural Strength
12000 psi
83 MPa
D 790
Flexural Modulus
0.33 x 10^6 psi
2275 MPa
D 790
ELECTRICAL
Volume Resistivity
> 1E16 ohm.cm
> 1E16 ohm.cm
D 257
THERMAL
Deflection Temperature
@ 264 psi (1820 kPa)
260 °F
127 °C
D 648
@ 66 psi (455 kPa)
270 °F
132 °C
D 648
Ignition Resistance*
Flammability
V-0 @ 1/16 in
V-0 @ 1.5 mm
UL94
Flammability
V-0 @ 1/8 in
V-0 @ 3.0 mm
UL94
PROPERTY NOTES
Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.
* This rating is not intended to reflect hazards of this or any other material under actual fire conditions.