點(diǎn)擊圖片查看大圖
ULTEM?
1000R resin
聚醚酰亞胺
產(chǎn)品說(shuō)明:
ULTEM 1000R resin is an amorphous, opaque polyetherimide (PEI) plastic
offering a glass transition temperature (Tg) of 217°C. This inherently flame
retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS compliant. ULTEM
1000R resin is an unreinforced general purpose grade offering high heat
resistance, high strength and modulus and broad chemical resistance up to high
temperatures with standard flow and standard mold
release.
| 塑料商城 | 塑料報(bào)價(jià)網(wǎng) | PDF數(shù)據(jù)表 | UL 黃卡 |
| 總體 | ||||
|
材料狀態(tài)
|
|
|||
|
資料 1
|
||||
|
UL 黃卡 2
|
||||
|
搜索 UL 黃卡
|
|
|||
|
供貨地區(qū)
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
外觀
|
|
|||
|
加工方法
|
|
|||
|
多點(diǎn)數(shù)據(jù)
|
|
| 物理性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
比重
|
1.27
|
g/cm3
|
ASTM D792 |
|
熔流率（熔體流動(dòng)速率） (337°C/6.6
kg)
|
9.7
|
g/10 min
|
ASTM D1238 |
|
收縮率 - 流動(dòng) (3.20 mm)
|
0.50 到 0.70
|
%
|
內(nèi)部方法 |
|
吸水率
|
ASTM D570 | ||
|
24
hr
|
0.25
|
%
|
|
|
平衡,
23°C
|
1.3
|
%
|
|
| 硬度 |
額定值
|
單位制
|
測(cè)試方法
|
|
洛氏硬度 (M 級(jí))
|
109
|
|
ASTM D785 |
| 機(jī)械性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
拉伸模量 3
|
3590
|
MPa
|
ASTM D638 |
|
抗張強(qiáng)度 4 (屈服)
|
110
|
MPa
|
ASTM D638 |
|
伸長(zhǎng)率 4
|
ASTM D638 | ||
|
屈服
|
7.0
|
%
|
|
|
斷裂
|
60
|
%
|
|
|
彎曲模量 5 (100 mm 跨距)
|
3520
|
MPa
|
ASTM D790 |
|
彎曲強(qiáng)度 5 (屈服, 100 mm
跨距)
|
165
|
MPa
|
ASTM D790 |
|
泊松比
|
0.36
|
|
ASTM D638 |
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17
轉(zhuǎn)輪)
|
10.0
|
mg
|
ASTM D1044 |
| 沖擊性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
懸壁梁缺口沖擊強(qiáng)度 (23°C)
|
53
|
J/m
|
ASTM D256 |
|
無(wú)缺口懸臂梁沖擊 (23°C)
|
1300
|
J/m
|
ASTM D4812 |
|
反向缺口沖擊 (3.20 mm)
|
1600
|
J/m
|
ASTM D256 |
|
落錘沖擊 (23°C)
|
36.6
|
J
|
ASTM D3029 |
| 熱性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
載荷下熱變形溫度
|
ASTM D648 | ||
|
0.45 MPa,
未退火, 6.40 mm
|
210
|
°C
|
|
|
1.8 MPa,
未退火, 6.40 mm
|
201
|
°C
|
|
|
維卡軟化溫度
|
219
|
°C
|
ASTM D1525 6 |
|
線形熱膨脹系數(shù)
|
ASTM E831 | ||
|
流動(dòng) : -20 到
150°C
|
5.6E-5
|
cm/cm/°C
|
|
|
橫向 : -20 到
150°C
|
5.4E-5
|
cm/cm/°C
|
|
|
導(dǎo)熱系數(shù)
|
0.22
|
W/m/K
|
ASTM C177 |
|
RTI Elec
|
170
|
°C
|
UL 746 |
|
RTI Imp
|
170
|
°C
|
UL 746 |
|
RTI
|
170
|
°C
|
UL 746 |
| 電氣性能 |
額定值
|
單位制
|
測(cè)試方法
|
|
體積電阻率
|
1.0E+17
|
ohms·cm
|
ASTM D257 |
|
介電強(qiáng)度
|
ASTM D149 | ||
|
1.60 mm, in
Air
|
33
|
kV/mm
|
|
|
1.60 mm, in
Oil
|
28
|
kV/mm
|
|
|
介電常數(shù) (1 kHz)
|
3.15
|
|
ASTM D150 |
|
耗散因數(shù)
|
ASTM D150 | ||
|
1
kHz
|
1.3E-3
|
|
|
|
2.45
GHz
|
2.5E-3
|
|
|
|
耐電弧性 7
|
PLC 5
|
|
ASTM D495 |
|
相比耐漏電起痕指數(shù)(CTI)
|
PLC 4
|
|
UL 746 |
|
高電弧燃燒指數(shù)(HAI)
|
PLC 3
|
|
UL 746 |
|
高電壓電弧起痕速率 (HVTR)
|
PLC 2
|
|
UL 746 |
|
熱絲引燃 (HWI)
|
PLC 1
|
|
UL 746 |
| 可燃性 |
額定值
|
單位制
|
測(cè)試方法
|
|
UL 阻燃等級(jí)
|
UL 94 | ||
|
0.400
mm
|
V-2
|
|
|
|
0.750
mm
|
V-0
|
|
|
|
3.00
mm
|
5VA
|
|
|
|
極限氧指數(shù)
|
47
|
%
|
ASTM D2863 |
|
NBS Smoke Density - Flaming,
Ds, 4 min
|
0.700
|
|
ASTM E662 |
| 注射 |
額定值
|
單位制
|
|
|
干燥溫度
|
149
|
°C
|
|
|
干燥時(shí)間
|
4.0 到 6.0
|
hr
|
|
|
干燥時(shí)間,，大
|
24
|
hr
|
|
|
建議的大水分含量
|
0.020
|
%
|
|
|
建議注射量
|
40 到 60
|
%
|
|
|
料筒后部溫度
|
332 到 399
|
°C
|
|
|
料筒中部溫度
|
338 到 399
|
°C
|
|
|
料筒前部溫度
|
343 到 399
|
°C
|
|
|
射嘴溫度
|
343 到 399
|
°C
|
|
|
加工（熔體）溫度
|
349 到 399
|
°C
|
|
|
模具溫度
|
135 到 163
|
°C
|
|
|
背壓
|
0.345 到 0.689
|
MPa
|
|
|
螺桿轉(zhuǎn)速
|
40 到 70
|
rpm
|
|
|
排氣孔深度
|
0.025 到 0.076
|
mm
|
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供,，內(nèi)容的真實(shí)性,、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé),，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任,。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份,，切勿隨意打款或發(fā)貨,，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息,，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào),。