點(diǎn)擊圖片查看大圖
產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 霧度2 | 40 mil | ASTM D-1003 | 76.1 | % |
| 硬度2 | Shore A,15 sec | ASTM D-2240 | >90 | ||
| 密度 | ExxonMobil Method | 0.902 | g/cm3 | ||
| 熔體流動(dòng)速率 | ExxonMobil Method | 2.5 | g/10 min | ||
| 硬度2 | Shore D,15 sec | ASTM D-2240 | 36.8 | ||
| 熔融指數(shù) | ExxonMobil Method | 1.1 | g/10 min | ||
| 物理性能 | 彎曲模量 | 1% secant | ASTM D-790 | 9842(67.9) | psi(MPa) |
| 沖擊強(qiáng)度 | 23℃ | ASTM D-256 | No Break | ft-lb/in(J/m) | |
| 沖擊強(qiáng)度 | -40℃ | ASTM D-256 | No Break | ft-lb/in(J/m) | |
| 拉伸強(qiáng)度3 | @Break | ASTM D-638 | No Break | psi(MPa) | |
| 拉伸率 | @Break | ASTM D-638 | No Break | % | |
| 熱性能 | 高熔體溫度 | ExxonMobil Method | 206.4(96.9) | ?H(℃) | |
| 維卡軟化點(diǎn)2 | 1000g | ASTM D-1525 | 182.7(83.7) | ℉(℃) | |
| 維卡軟化點(diǎn)2 | 200g | ASTM D-1525 | 205.2(96.2) | ℉(℃) | |
| 其它性能 | 拉應(yīng)力5 | @ Elongation | ASTM D-412 | 1780(12.3) | psi(MPa) |
| 拉伸率 | @Break | ASTM D-412 | 1144 | % | |
| 抗扯強(qiáng)度 | ASTM D-624 | 508.5(89.1) | lb-in(kN/m) | ||
| 拉伸強(qiáng)度 | @Peak | ASTM D-412 | 4454(30.7) | psi(MPa) | |
| 門(mén)尼粘度ML(1+4) | 125℃ | ASTM D-1646 | 3.9 | Torgue Units | |
| 抗環(huán)境應(yīng)力開(kāi)裂性 | ASTM D-1693 | >1000 | hr | ||
| 拉應(yīng)力5 | @300% Elongation | ASTM D-412 | 2115(14.6) | psi(MPa) | |
?
用途說(shuō)明
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供,，內(nèi)容的真實(shí)性,、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任,。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家,，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨,，謹(jǐn)防上當(dāng)受騙,。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào),。