| SABIC Innovative Plastics LNP STAT-KON Lexan_JK2500 PC+ABS | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer; Polycarbonate/ABS Alloy, Carbon Fiber Filled; Polycarbonate (PC)
|
||
| Material Notes: |
LNP* Stat-kon* Lexan_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow |
0.00060 - 0.0015 cm/cm @Thickness 3.20 mm |
0.00060 - 0.0015 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse |
0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow |
25 g/10 min @Load 1.20 kg, Temperature 300 °C |
25 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 11.03 GPa | 1600 ksi | 5 mm/min; ASTM D638 |
| 11.13 GPa | 1614 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
| 112 MPa | 16200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.23 GPa | 1340 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.09 GPa | 1463 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.24 J/cm | 4.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy |
14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.0 ohm-cm | 2.0 ohm-cm | ASTM D257 |
| Surface Resistance | 10000 ohm | 10000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow 
|
12.6 μm/m-°C @Temperature -40.0 - 40.0 °C |
7.00 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
80.0 μm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
|
CTE, linear, Transverse to Flow
|
63.0 μm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
77.0 μm/m-°C @Temperature 23.0 - 80.0 °C |
42.8 μin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) |
98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
Deflection Temperature at 1.8 MPa (264 psi)
|
93.0 °C @Thickness 3.20 mm |
199 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
96.0 °C @Thickness 6.40 mm |
205 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 100 °C | 212 °F | Rate B/120; ISO 306 |
| 111 °C | 232 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 |
V-0 @Thickness 0.990 mm |
V-0 @Thickness 0.0390 in |
UL 94 |
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
SABIC Innovative Plastics LNP STAT-KON Cycoloy_JK800 PC+ABS
305 Stainless Steel, annealed, sheet
Lehmann & Voss LUVOCOM? 1106-8088/RD Polyether imide, unreinforced, laser markable
Lehmann & Voss LUVOCOM? 1106-8089/BL Polyether imide, unreinforced, laser markable
LNP VALOX? EXCP0099 Polybutylene Terephthalate, 20% Carbon Fiber Reinforcement
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性,、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé),，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任,。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家,，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份,，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙,。如發(fā)現(xiàn)虛假信息,，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。